Under normal circumstances, the plated parts processed by aluminum profiles must be inspected before they are received and produced. If it is a large number of small pieces, it is generally a random inspection. If it is a large piece or an important product, then generally each piece should be carefully checked to prevent defective products from entering the production line.

Some assembled parts cannot be plated into the tank, because the solution may enter the gap, causing danger. If electroplating must be carried out, then some insulation protection must be added, or a treatment method such as brush plating must be selected.

 

The main purpose of silver plating on aluminum is to deal with the metal bonding force of the coating and the substrate. In this process, some precautions need to be paid attention to. Let's learn about it together with Hongyong Precision, an aluminum product processing factory:

 

1. Whether it is degreasing or alkaline washing, the content of cyanide should not be too high to prevent corrosion on the surface.

 

2. The galvanizing process needs to be carried out twice, because after the first galvanizing, the zinc layer will be relatively rough, so it is necessary to carry out the second time, and galvanizing is the key to whether a satisfactory coating can be obtained, so , Be careful when galvanizing.

 

3. Pay attention to swinging during the galvanizing process to avoid parts stacking on each other and causing a part without zinc layer.

 

4. If it is found that the galvanizing quality of some products is not good after the galvanizing is completed, then 1:1 HNO can be used, and then the galvanizing can be restarted after removing it.

 

5. When the parts after dipping galvanize enter the high-quality copper plating solution, they should be charged into the tank, and after 2 minutes of impact plating with a large current, return to the normal current. In the process of electroplating, if it is found that the appearance of some parts is black and dark, the parts can be taken out and processed before electroplating.